sažetak izlaganja sa skupa
Objectives: The objective of this research was to investigate compressive strength, breaking strength and compressive modulus of glass hybrid restorative material modified with TiO 2 nano particles (NP), hydroxyapatite (HAp) particles (<45µm) and a combination of TiO 2 NP and HAp particles. Methods: Materials used in the study were glass hybrid material Equia Forte HT Fil (GC Corporation, Tokyo, Japan), TiO 2 powder P25 (Degussa, Essen, Germany) and HAp synthesized from cuttlefish bone and grounded in a mortar to obtain HAp powder. There were four groups of samples (N=10): (i) Equia Forte HT control group ; (ii) modified with 3 wt% TiO 2 ; (iii) modified with 3 wt% HAp and (iv) modified with 1.5wt%TiO2 + 1.5wt%Hap (Figure 1). Measurements were performed in the universal testing machine and compressive strength (CS), breaking strength (BS) and compressive modulus (CM) were calculated for the four groups of samples (Figures 2 and 3). Statistical analysis was performed using ANOVA and Tukey test and the equality of variances was tested using Leven test.Results: CS, BS and CM differed significantly between the groups (ANOVA test, p = 0.008, p = 0.004 and p = 0.0001, respectively), (Table 1). CS and BS were significantly higher in 3wt% HAp group than in other two experimental groups (3wt%TiO 2 and 1.5wt%TiO 2 + 1.5wt%HAp groups), (Table 1). CM was significantly higher in 3wt% HAp group compared to the control group and 1.5wt%TiO 2 + 1.5wt%HAp group (Table 1).Conclusions: Equia Forte HT Fil with 3wt% HAp micro particles added to the original powder showed improved CS and BS, and CM was significantly higher compared to the control group.
HAp ; TiO2 ; compressive strength ; glass hybrid
Razvojem virtualizacijskih tehnologija raste kompleksnost IT sustava, dok korisnici istovremeno zahtijevaju brži pristup resursima, napredne integracije i jednostavnost korištenja. Jedno od ključnih rješenja za ove izazove primjena je…
Ovaj rad istražuje i uspoređuje mogućnosti prosljeđivanja grafičkih kartica na Hyper-V i KVM hipervizorima prema virtualnim strojevima, detaljno opisujući metode, postupke i razlike u arhitekturi koje utječu na…
The ever-growing usage and adaptation of HTTP/3 in web traffic leverages Quick UDP Internet Connections (QUIC) as a transport protocol. QUIC is widely recognized for reduced latency, enhanced…