izvorni znanstveni rad
The contribution compares the abrasion and erosion resistance of twohigh-alloy tool steels, X153CrMoV12-1 and Böhler K390 Micro Clean, coated with multilayer coatings TiN/TiCN and TiN/Ti-B-N. Multilayer coatings were applied to hardened and tempered samples by pulsed direct current (DC) plasma-assisted chemical-vapour deposition (PACVD) process in the Rübig PC 70/90 industrial vacuum furnace. The mechanical properties of the coating were tested by calottest, Rockwell-C indentation and the micro hardness tests. Abrasion resistance was tested by the “Dry sand/Rubber wheel” and micro abrasion method. Erosion resistance was tested by exposing the surface of the samples to a jet of fine sand particles at an angle of incidence of 90 degrees for 60min. Worn surfaces were analysed with a light and scanning electron microscope. It was found that increased resistance to abrasion and erosion wear is achieved on samples with higher substrate hardness and higher hardness, and better adhesion of the coating.
DC PACVD; TiN/TiCN coating; TiN/Ti-B-N coating; K390 micro clean; X153CrMoV12-1; abrasion resistance; erosion resistance; calottest
Razvojem virtualizacijskih tehnologija raste kompleksnost IT sustava, dok korisnici istovremeno zahtijevaju brži pristup resursima, napredne integracije i jednostavnost korištenja. Jedno od ključnih rješenja za ove izazove primjena je…
Ovaj rad istražuje i uspoređuje mogućnosti prosljeđivanja grafičkih kartica na Hyper-V i KVM hipervizorima prema virtualnim strojevima, detaljno opisujući metode, postupke i razlike u arhitekturi koje utječu na…
The ever-growing usage and adaptation of HTTP/3 in web traffic leverages Quick UDP Internet Connections (QUIC) as a transport protocol. QUIC is widely recognized for reduced latency, enhanced…